PIC 100 M

EnvisionTEC PIC100 M and PIC100G M resins have been developed for direct investment casting of products for the jewelry market. They offer excellent burn out properties and build with the highest quality and crisp detail. The materials may processed on all Perfactory® systems. Parts made using EnvisionTEC PIC100 M resins evaporate at moderate burn out temperatures without reacting with your investment and offer an extremely low thermal expansion. It is optimally suitable for producing precious metal castings. EnvisionTEC PIC100 M builds extremely smooth surfaces.

The burn out process is ash free allowing for a casting which is free from porosity, a problem which is a result of the ash residue when burning a polymer based material. EnvisionTEC PIC100 M is a photo cured resin that produces the highest quality details without sacrificing toughness, ease of handling, and finishing. Highest quality details, standard burn out procedure, and high speed building qualify EnvisionTEC PIC100 M resins for producing high quality parts in the jewelry market for production capacity direct investment casting.

Physical Properties

Viscosity

361.7 mPa*s (ASTM Method DIN 1342-2)

Tensile Strength

16.8 MPa (ASTM Method DIN EN ISO 527-1)

Elongation at Break

7.46 % (ASTM Method DIN EN ISO 527-1)

Flexural Strength

23.0 MPa (ASTM Method DIN EN ISO 178)

Flexural Modulus

404.0 MPa (ASTM Method DIN EN ISO 178)

Bending Strain

10.2 % (ASTM Method DIN EN ISO 178)

Izod Impact-Notched

11.03 kJ/m2 (ASTM Method DIN EN ISO 180)

Density

1.178 g/cm3 (ASTM Method DIN ISO 1183-1)

Hardness (Shore D)

69 Shore (ASTM Method DIN EN ISO 868)

Ignition Temperature

350 °C (ASTM Method DIN 53765)